文摘
[100] is believed to be a tough diffusion direction for Li+ in LiFePO4, leading to the belief that the rate performance of [100]-oriented LiFePO4 is poor. Here we report the fabrication of 12 nm-thick [100]-oriented LiFePO4 nanoflakes by a simple one-pot solvothermal method. The nanoflakes exhibit unexpectedly excellent electrochemical performance, in stark contrast to what was previously believed. Such an exceptional result is attributed to a decreased thermodynamic transformation barrier height (Δμb) associated with increased active population.