Sulfur Embedded in a Mesoporous Carbon Nanotube Network as a Binder-Free Electrode for High-Performance Lithium–Sulfur Batteries

详细信息    查看全文

• 作者：Li Sun ; Datao Wang ; Yufeng Luo ; Ke Wang ; Weibang Kong ; Yang Wu ; Lina Zhang ; Kaili Jiang ; Qunqing Li ; Yihe Zhang ; Jiaping Wang ; Shoushan Fan
• 刊名：ACS Nano
• 出版年：2016
• 出版时间：January 26, 2016
• 年：2016
• 卷：10
• 期：1
• 页码：1300-1308
• 全文大小：501K
• ISSN：1936-086X

文摘

Sulfur-porous carbon nanotube (S-PCNT) composites are proposed as cathode materials for advanced lithium–sulfur (Li–S) batteries. Abundant mesopores are introduced to superaligned carbon nanotubes (SACNTs) through controlled oxidation in air to obtain porous carbon nanotubes (PCNTs). Compared to original SACNTs, improved dispersive behavior, enhanced conductivity, and higher mechanical strength are demonstrated in PCNTs. Meanwhile, high flexibility and sufficient intertube interaction are preserved in PCNTs to support binder-free and flexible electrodes. Additionally, several attractive features, including high surface area and abundant adsorption points on tubes, are introduced, which allow high sulfur loading, provide dual protection to sulfur cathode materials, and consequently alleviate the capacity fade especially during slow charge/discharge processes. When used as cathodes for Li–S batteries, a high sulfur loading of 60 wt % is achieved, with excellent reversible capacities of 866 and 526 mAh g^–1 based on the weights of sulfur and electrode, respectively, after 100 cycles at a slow charge/discharge rate of 0.1C, revealing efficient suppression of polysulfide dissolution. Even with a high sulfur loading of 70 wt %, the S-PCNT composite maintains capacities of 760 and 528 mAh g^–1 based on the weights of sulfur and electrode, respectively, after 100 cycles at 0.1C, outperforming the current state-of-the-art sulfur cathodes. Improved high-rate capability is also delivered by the S-PCNT composites, revealing their potentials as high-performance carbon–sulfur composite cathodes for Li–S batteries.