Porous Core–Shell Fe3C Embedded N-doped Carbon Nanofibers as an Effective Electrocatalysts for Oxygen Reduction Reaction

详细信息    查看全文

• 作者：Guangyuan Ren ; Xianyong Lu ; Yunan Li ; Ying Zhu ; Liming Dai ; Lei Jiang
• 刊名：ACS Applied Materials & Interfaces
• 出版年：2016
• 出版时间：February 17, 2016
• 年：2016
• 卷：8
• 期：6
• 页码：4118-4125
• 全文大小：494K
• ISSN：1944-8252

文摘

The development of nonprecious-metal-based electrocatalysts with high oxygen reduction reaction (ORR) activity, low cost, and good durability in both alkaline and acidic media is very important for application of full cells. Herein, we developed a facile and economical strategy to obtain porous core–shell Fe₃C embedded nitrogen-doped carbon nanofibers (Fe₃C@NCNF-X, where X denotes pyrolysis temperature) by electrospinning of polyvinylidene fluoride (PVDF) and FeCl₃ mixture, chemical vapor phase polymerization of pyrrole, and followed by pyrolysis of composite nanofibers at high temperatures. Note that the FeCl₃ and polypyrrole acts as precursor for Fe₃C core and N-doped carbon shell, respectively. Moreover, PVDF not only plays a role as carbon resources, but also provides porous structures due to hydrogen fluoride exposure originated from thermal decomposition of PVDF. The resultant Fe₃C@NCNF-X catalysts, particularly Fe₃C@NCNF-900, showed efficient electrocatalytic performance for ORR in both alkaline and acidic solutions, which are attributed to the synergistic effect between Fe₃C and N-doped carbon as catalytic active sites, and carbon shell protects Fe₃C from leaching out. In addition, the Fe₃C@NCNF-X catalyst displayed a better long-term stability, free from methanol crossover and CO-poisoning effects than those of Pt/C, which is of great significance for the design and development of advanced electrocatalysts based on nonprecious metals.