Mechanistic Studies of Pd(II)-Catalyzed Copolymerization of Ethylene and Vinylalkoxysilanes: Evidence for a β-Silyl Elimination Chain Transfer Mechanism

详细信息    查看全文

• 作者：Zhou Chen ; Weijun Liu ; Olafs Daugulis ; Maurice Brookhart
• 刊名：Journal of the American Chemical Society
• 出版年：2016
• 出版时间：December 14, 2016
• 年：2016
• 卷：138
• 期：49
• 页码：16120-16129
• 全文大小：543K
• ISSN：1520-5126

文摘

Copolymerizations of ethylene with vinyltrialkoxysilanes are reported using both a “traditional” cationic Pd(II) aryldiimine catalyst, t-1 (aryl = 2,6-diisopropylphenyl), and a “sandwich-type” aryldiimine catalyst, s-2 (aryl = 8-tolylnaphthyl). Incorporation levels of vinyltrialkoxysilanes between 0.25 and 2.0 mol % were achieved with remarkably little rate retardation relative to ethylene homopolymerizations. In the case of the traditional catalyst system, molecular weights decrease as the level of comonomer increases and only one trialkoxysilyl group is incorporated per chain. Molecular weight distributions of ca. 2 are observed. For the sandwich catalyst, higher molecular weights are observed with many more trialkoxysilyl groups incorporated per chain. Polymers with molecular weight distributions of ca. 1.2–1.4 are obtained. Detailed NMR mechanistic studies have revealed the formation of intermediate π-complexes of the type (diimine)Pd(alkyl)(vinyltrialkoxysilane)⁺. 1,2-Migratory insertions of these complexes occur with rates similar to ethylene insertion and result in formation of observable five-membered chelate intermediates. These chelates are rapidly opened with ethylene forming alkyl ethylene complexes, a requirement for chain growth. An unusual β-silyl elimination mechanism was shown to be responsible for chain transfer and formation of low molecular weight copolymers in the traditional catalyst system, t-1. This chain transfer process is retarded in the sandwich system. Relative binding affinities of ethylene and vinyltrialkoxysilanes to the cationic palladium center have been determined. The quantitative mechanistic studies reported fully explain the features of the bulk polymerization results.