Resistance Switching Characteristics Induced by O2 Plasma Treatment of an Indium Tin Oxide Film for Use as an Insulator in Resistive Random Access Memory
详细信息    查看全文
文摘
In this study, an O2 inductively coupled plasma (ICP) treatment was developed in order to modify the characteristics of indium tin oxide (ITO) film for use as an insulator in resistive random access memory (RRAM). After the O2 plasma treatment, the previously conductive ITO film is oxidized and becomes less conductive. In addition, after capping the same ITO material for use as a top electrode, we found that the ITO/ITO(O2 plasma)/TiN device exhibits very stable and robust resistive switching characteristics. On the contrary, the nontreated ITO film for use as an insulator in the ITO/ITO/TiN device cannot perform resistance switching behaviors. The material analysis initially investigated the ITO film characteristics with and without O2 plasma treatment. The surface was less rough after O2 plasma treatment. However, the molar concentration of each element and measured sheet resistance results for the O2-plasma-treated ITO film were dramatically modified. Next, electrical measurements were carried out to examine the resistance switching stability under continuous DC and AC operation in this ITO/ITO(O2 plasma)/TiN device. Reliability tests, including endurance and retention, also proved its capability for use in data storage applications. In addition to these electrical measurements, current fitting method experiments at different temperatures were performed to examine and confirm the resistance switching mechanisms. This easily fabricated device, using a simple material combination, achieves excellent performance by using ITO with an O2 plasma treatment and can further the abilities of RRAM for use in remarkable potential applications.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700