Synthesis and characterization of Li₂TiSiO₅ obtained by melting and solid-state reaction

详细信息    查看全文

• 作者：M. T. Souza ; F. R. Cesconeto ; S. Arcaro…
• 关键词：Synthesis processes ; Thermal analysis ; Heat treatments ; Crystallographic analysis
• 刊名：Journal of Thermal Analysis and Calorimetry
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：127
• 期：1
• 页码：463-467
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Physical Chemistry; Analytical Chemistry; Polymer Sciences; Inorganic Chemistry; Measurement Science and Instrumentation;
• 出版者：Springer Netherlands
• ISSN：1588-2926
• 卷排序：127

文摘

In this work, the synthesis of the Li₂TiSiO₅ photoluminescent compound, obtained from a stoichiometric mixture of Li₂CO₃, SiO₂ and TiO₂ nanoparticles, was investigated by two different routes named route I (melting and quenching) and route II (solid-state reaction). In the route I, the raw materials were melted (1550 °C/2 h) and cooled into water. Subsequently, the solidified product was milled (30 min) in a high-energy mill. In the route II, the raw materials were directly milled (10 min). The obtained powders, from both routes, were heat treated at different temperatures (900–1000 °C/60 min) and then subjected to crystallographic (XRD) and thermal (DSC) analyses in order to investigate the resulting structure and the associated physical–chemical reactions. The results showed that it is possible to obtain the Li₂TiSiO₅ compound from both synthesis routes but, apparently, the route I seems to be more appropriated to obtain the Li₂TiSiO₅ compound and to demonstrate the photoluminescence phenomena with and even without thermal treatment.