Corrosion inhibition and surface analysis of amines on mild steel in chloride medium

详细信息    查看全文

• 作者：Klodian Xhanari ; Natalija Grah ; Matjaž Finšgar ; Regina Fuchs-Godec…
• 关键词：Steel ; Corrosion ; Corrosion inhibitor ; Amines ; Surface analysis
• 刊名：Chemical Papers
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：71
• 期：1
• 页码：81-89
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Chemistry/Food Science, general; Industrial Chemistry/Chemical Engineering; Biochemistry, general; Medicinal Chemistry; Materials Science, general; Biotechnology;
• 出版者：Springer International Publishing
• ISSN：1336-9075
• 卷排序：71

文摘

In this study, the corrosion inhibition effectiveness of eight amines, i.e. 2-ethylhexyl amine, aniline, benzylamine, butylamine, ethylamine, isopropylamine, octylamine, and triethanolamine, on C15 grade mild steel in 3 wt% NaCl solution is reported. The corrosion inhibition performance of the amines was studied using immersion tests at 25 and 70 °C, with and without the addition of KI as a possible intensifier. Among the inhibitors tested at 0.1 wt% concentration, the lowest corrosion rates were obtained for specimens immersed in solutions containing 2-ethylhexyl amine at 25 °C and triethanolamine at 70 °C. The highest inhibition effectiveness at 25 °C among all amines tested was obtained for 1.0 wt% butylamine with the addition of 0.5 wt% KI, while at 70 °C the lowest corrosion rate was obtained for specimens inhibited with 1.0 wt% isopropylamine. Surface analysis was subsequently performed on specimens inhibited by the most effective inhibitors. Adsorption of the selected amines on the C15 grade mild steel surface was confirmed by ATR-FTIR. 3D-profilometry showed a reduction in the surface roughness (less corroded) for the specimens inhibited with these inhibitors compared to the non-inhibited specimens. Contact angle measurements showed that all of the tested specimens were hydrophilic.