Low-temperature synthesis of hierarchical architectures of SAPO-11 zeolite as a good hydroisomerization support

详细信息    查看全文

• 作者：Zhou Chen ; Yunyun Dong ; Shaoyang Jiang ; Wenjing Song&#8230
• 刊名：Journal of Materials Science
• 出版年：2017
• 出版时间：April 2017
• 年：2017
• 卷：52
• 期：8
• 页码：4460-4471
• 全文大小：
• 刊物类别：Chemistry and Materials Science
• 刊物主题：Materials Science, general; Characterization and Evaluation of Materials; Polymer Sciences; Continuum Mechanics and Mechanics of Materials; Crystallography and Scattering Methods; Classical Mechanics;
• 出版者：Springer US
• ISSN：1573-4803
• 卷排序：52

文摘

Hierarchical SAPO-11 was successfully synthesized without a secondary template by changing the hydrothermal crystallization temperature. SAPO-11 with a larger external surface area, more acidity, and a large number of external active sites was constructed through a novel two-step crystallization strategy. Both precrystallization step and the low-temperature crystallization step were confirmed to be indispensable conditions for constructing hierarchical SAPO-11. After loading Pt nanoparticles by incipient wetness impregnation, the heptane hydroisomerizations based on 0.5 wt% Pt/C-SAPO-11-200 and 0.5 wt% Pt/T-SAPO-11-120 catalysts were carried out in a fixed-bed at a total pressure of 1.5 MPa with a H₂/n-heptane volumetric of 400 and WHSV = 10 h−1. A conversion level of 75.7% of 0.5 wt% Pt/T-SAPO-11-120 catalyst was reached, which was higher than that of 0.5 wt% Pt/C-SAPO-11-200 catalyst (64.3%) at 300 °C. The enhanced performance achieved was attributed to the improved effect of the support, in terms of not only better mass transport and higher number of exposure active sites but also improved dispersity and decrease in the size of Pt particles.