x)Zr(30+x)Ti10 (x=0, 5, and 10 at%) amorphous alloys to the application of tension was investigated. The structural sensitivity to tension decreases with increasing Cu content. The crystallization enthalpy increases with increasing excess free volume. The characteristic temperatures of the tensile samples can surpass those of the as-cast ones under a critical heating rate which differs in the Cu content. The increase of the excess free volume significantly influences the glass transition and crystallization procedures." />
用户名: 密码: 验证码:
Structural and thermal sensitivity of Cu-Zr-Ti amorphous alloys to tension
详细信息    查看全文
  • 作者:AnHui Cai (15155) (25155)
    Xiang Xiong (25155)
    Yong Liu (25155)
    WeiKe An (15155)
    GuoJun Zhou (15155)
    Yun Luo (15155)
    TieLin Li (15155)
    XiaoSong Li (15155)
  • 关键词:Cu ; based amorphous alloy ; tension ; sensitivity
  • 刊名:SCIENCE CHINA Physics, Mechanics & Astronomy
  • 出版年:2013
  • 出版时间:August 2013
  • 年:2013
  • 卷:56
  • 期:8
  • 页码:1606-1610
  • 全文大小:701KB
  • 参考文献:1. Das J, Tang M B, Kim K B, et al. “Work-hardenable-ductile bulk metallic glass. Phys Rev Lett, 2005, 94: 205501 CrossRef
    2. Kim K H, Kin H J, Lee J C. Effect of a minor element with a large mixing enthalpy difference on the plasticity of amorphous alloys. J Mater Res, 2007, 22: 2558-564 CrossRef
    3. Pauly S, Liu G, Gorantla S, et al. Criteria for tensile plasticity in Cu-Zr-Al bulk metallic glasses. Acta Mater, 2010, 58: 4883-890 CrossRef
    4. Pan J, Chan K C, Chen Q, et al. The effect of microalloying on mechanical properties in Cu-Zr-Al bulk metallic glass. J Alloys Compd, 2010, 504: S74–S77 CrossRef
    5. Zhang W, Zhang Q S, Qin C L, et al. Formation and properties of new Cu-based bulk glassy alloys with critical diameter up to 1.5 cm. J Mater Res, 2009, 24: 2935-940 CrossRef
    6. Shen Y, Xu J. Improving plasticity and toughness of Cu-Zr-Y-Al bulk metallic glasses via compositional tuning towards the CuZr. J Mater Res, 2010, 25: 375-82 CrossRef
    7. Kim K B, Das J, Baier F, et al. Heterogeneity of a Cu<sub class="a-plus-plus">47.5sub>Zr<sub class="a-plus-plus">47.5sub>Al<sub class="a-plus-plus">5sub> bulk metallic glass. Appl Phys Lett, 2006, 88: 051911 CrossRef
    8. Mattern N, Vainio U, Park J M, et al. Phase separation in Cu<sub class="a-plus-plus">46sub>Zr<sub class="a-plus-plus">47?em class="a-plus-plus">x sub> Al<sub class="a-plus-plus">7sub>Gd<sub class="a-plus-plus">xsub> metallic glasses. J Alloys Compd, 2011, 509: S23–S26 CrossRef
    9. Zhang Q S, Zhang W, Xie G Q, et al. Formation of a phase separating bulk metallic glass in Cu<sub class="a-plus-plus">40sub>Zr<sub class="a-plus-plus">40sub>Al<sub class="a-plus-plus">10sub>Ag<sub class="a-plus-plus">10sub> alloy. Mater Sci Eng B, 2008, 148: 97-00 CrossRef
    10. Kovács Z, Révész á. Effect of local ordering on the decomposition of an amorphous Cu-Zr-Ti alloy. Appl Phys Lett, 2005, 87: 251909 CrossRef
    11. Cao Q P, Li J F, Zhou Y H, et al. Free-volume evolution and its temperature dependence during rolling of Cu<sub class="a-plus-plus">60sub>Zr<sub class="a-plus-plus">20sub>Ti<sub class="a-plus-plus">20sub> bulk metallic glass. Appl Phys Lett, 2005, 87:101901 CrossRef
    12. Park E S, Chang H J, Kim D H. Improvement of glass-forming ability and phase separation in Cu-Ti-rich Cu-Ti-Zr-Ni-Si bulk metallic glasses. J Alloys Compd, 2010, 504: S27–S30 CrossRef
    13. Pauly S, Das J, Mattern N, et al. Phase formation and thermal stability in Cu-Zr-Ti (Al) metallic glasses. Intermetallics, 2009, 17: 453-62 CrossRef
    14. Hóbor S, Révész á, Szabó P J, et al. High pressure torsion of amorphous Cu<sub class="a-plus-plus">60sub>Zr<sub class="a-plus-plus">30sub>Ti<sub class="a-plus-plus">10sub> alloy. J Appl Phys, 2008, 104: 033525 CrossRef
    15. Pauly S, Gorantla S, Wang G, et al. Transformation-mediated ductility in CuZr-based bulk metallic glasses. Nat Mater, 2010, 9: 473-77 CrossRef
    16. Molnár á, Domokos L, Katona T, et al. Activation of amorphous Cu- / M ( / M=Ti, Zr or Hf) alloy powders made by mechanical alloying. Mater Sci Eng A, 1997, 226-28: 1074-078
    17. Song K K, Pauly S, Zhang Y, et al. Significant tensile ductility induced by cold rolling in Cu<sub class="a-plus-plus">47.5sub>Zr<sub class="a-plus-plus">47.5sub>Al<sub class="a-plus-plus">5sub> bulk metallic glass. Intermetallics, 2011, 19: 1394-398 CrossRef
    18. Park J S, Kim J M, Park E S. Structural behaviors of single and multiple amorphous alloys deformed by forced cold rolling. Intermetallics, 2010, 18: 1920-924 CrossRef
    19. Cao Q P, Li J F, Zhou Y H, et al. Microstructure and microhardness evolutions of Cu<sub class="a-plus-plus">47.5sub>Zr<sub class="a-plus-plus">47.5sub>Al<sub class="a-plus-plus">5sub> bulk metallic glass processed by rolling. Scripta Mater, 2008, 59: 673-76 CrossRef
    20. Cai A H, An W K, Li X S, et al. Property of Cu-Zr-Ti ternary alloys. Adv Mater Res, 2011, 146-147: 1477-481 CrossRef
    21. Inoue A, Zhang W, Zhang T, et al. High-strength Cu-based bulk glassy alloys in Cu-Zr-Ti and Cu-Hf-Ti ternary systems. Acta Mater, 2001, 49: 2645-652 CrossRef
    22. Slipenyuk A, Eckert J. Correlation between enthalpy change and free volume reduction during structural relaxation of Zr<sub class="a-plus-plus">55sub>Cu<sub class="a-plus-plus">30sub>Al<sub class="a-plus-plus">10sub>Ni<sub class="a-plus-plus">5sub> metallic glass. Scripta Mater, 2004, 50: 39-4 CrossRef
    23. Khonik VA, Kitagawa K, Mori H. On the determination of the crystallization activation energy of metallic glasses. J Appl Phys, 2000, 87: 8440-443 CrossRef
  • 作者单位:AnHui Cai (15155) (25155)
    Xiang Xiong (25155)
    Yong Liu (25155)
    WeiKe An (15155)
    GuoJun Zhou (15155)
    Yun Luo (15155)
    TieLin Li (15155)
    XiaoSong Li (15155)

    15155. College of Mechanical Engineering, Hunan Institute of Science and Technology, Yueyang, 414000, China
    25155. State Key Laboratory of Powder Metallurgy, Central South University, Changsha, 410083, China
文摘
Structural and thermal sensitivity of Cu(60?em class="a-plus-plus">x)sub>Zr(30+x)sub>Ti10sub> (x=0, 5, and 10 at%) amorphous alloys to the application of tension was investigated. The structural sensitivity to tension decreases with increasing Cu content. The crystallization enthalpy increases with increasing excess free volume. The characteristic temperatures of the tensile samples can surpass those of the as-cast ones under a critical heating rate which differs in the Cu content. The increase of the excess free volume significantly influences the glass transition and crystallization procedures.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700